Energetic conditions for interfacial failure in the vicinity of a matrix crack in brittle matrix composites

DOI10.1016/j.ijsolstr.2004.05.044zbMath1181.74113OpenAlexW2013101360MaRDI QIDQ2571900

Dominique Leguillon, Eric Martin

Publication date: 14 November 2005

Published in: International Journal of Solids and Structures (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1016/j.ijsolstr.2004.05.044

zbMATH Keywords

Crack deflectionInterfacial debondingCeramic matrix compositeEnergetic analysis

Mathematics Subject Classification ID

Brittle fracture (74R10)

Related Items (4)

Crack propagation in non-homogenous materials: evaluation of mixed-mode SIFs, T-stress and kinking angle using a variant of EFG method ⋮ Application of the coupled stress-energy criterion to predict the fracture behaviour of layered ceramics designed with internal compressive stresses ⋮ Stress state characterization of delamination cracks in [0/90 symmetric laminates by BEM] ⋮ Competition between deflection and penetration at an interface in the vicinity of a main crack

This page was built for publication: Energetic conditions for interfacial failure in the vicinity of a matrix crack in brittle matrix composites