A crack in functionally gradient materials under thermal shock

MaRDI QIDQ1323046zbMATH OpenFDO

Authors V. Pereyra

Publication date 10 May 1994

Published in Archive of Applied Mechanics (Search for Journal in Brave)

zbMATH Keywords

Fourier transformLaplace transformsingular integral equationstress intensity factortwo bonded semi-infinite plates

Mathematics Subject Classification ID

Stress concentrations, singularities in solid mechanics (74G70) Fracture and damage (74R99)

Recommendations

• Transient thermal stress intensity factors for a crack in a semi-infinite plate of a functionally gradient material
• Thermal shock analysis for a functionally graded plate with a surface crack
• Thermal stress intensity factors for a crack in a strip of a functionally gradient material
• Thermal fracture of functionally gradient ceramics
• Thermal stress intensity factor for functionally gradient half space with an edge crack under thermal load

Cited in

(27)

• Heat conduction analysis of 3-D axisymmetric and anisotropic FGM bodies by meshless local Petrov-Galerkin method
• Thermal stress intensity factors for a crack in a strip of a functionally gradient material
• Stress analysis in a joint with a functionally graded material under a thermal loading by using the Mellin transform method
• Transient thermal stress intensity factors for a crack in a semi-infinite plate of a functionally gradient material
• Crack channeling and spalling in a plate due to thermal shock loading
• Edge crack problem in a semi-infinite FGM plate with a bi-directional coefficient of thermal expansion under two-dimensional thermal loading
• A preparation method of functionally graded materials with phase transition under shock loading
• Thermal shock fracture of a crack in a functionally gradient half-space based on the memory-dependent heat conduction model
• Thermal fracture of functionally gradient ceramics
• Crack closure effects in thermal fracture of functionally graded/homogeneous bimaterials with systems of cracks
• Non-symmetric thermal shock in ceramic matrix composite (CMC) materials
• The integral equation method on the fracture of FGCMs
• Thermal stress intensity factors for an interface crack in a functionally graded layered structures
• Initiation of a periodic array of cracks in the thermal shock problem: A gradient damage modeling
• Coupled thermoelasticity of a functionally graded cracked layer under thermomechanical shocks
• A periodic array of cracks in functional graded materials subjected to thermo-mechanical loading
• Edge-cracked bimaterial systems under thermal heating
• Thermal fracture characteristics induced by laser beam.
• Thermal stress intensity factor for functionally gradient half space with an edge crack under thermal load
• Stress-intensity factors for surface cracks in functionally graded materials under mode-I thermomechanical loading
• Theoretical analysis of heat conduction problems of nonhomogeneous functionally graded materials for a layer sandwiched between two half-planes
• Transient heat conduction in a functionally graded strip in contact with well stirred fluid with an outside heat source
• Inverse heat conduction problems in three-dimensional anisotropic functionally graded solids
• Effects of multiple cracking on the residual strength behavior of thermally shocked functionally graded ceramics
• Thermal shock analysis for a functionally graded plate with a surface crack
• The effect of oblique functional gradation to thermal stresses in the functionally graded infinite strip
• Estimation of the crack length after thermal shock in FGM strip

This page was built for publication: A crack in functionally gradient materials under thermal shock

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q1323046)