DOI10.5281/zenodo.10359930Zenodo10359930MaRDI QIDQ6711050FDOQ6711050
Dataset published at Zenodo repository.
Markus Mehnert, Miguel Angel Moreno Mateos, Paul Steinmann
Publication date: 12 December 2023
Copyright license: Creative Commons Attribution 4.0 International
This dataset contains the experimental raw data from the mechanical and electro-mechanical testing of soft dielectric elastomers: unfilled PDMS and BaTiO3-filled PDMS. The data have not been filtered. Every specimen is tested under tensile loading until full rupture.All specimens had a thickness of 3mm. The initial length between grips was set to 40mm. The files are named according to:- the type of sample (Unfilled_PDMS/BaTiO3_Filled),- the width of the sample (w30mm/w50mm),- the length of the pre-cut (c0mm/c3mm/c5mm/c6mm/c9mm/c10mm/c12mm/c15mm/c20mm/c25mm),- the voltage applied in the thickness direction during tensile deformation (0kV/4kV/8kV),- and the number of the experiment up to the total number of repetitions under the same test conditions (R1/R2/R3 for filled samples and R1/R2 for unfilled samples). If this dataset is used for research or industrial purposes, please cite:M.A. Moreno-Mateos, M. Mehnert, P. Steinmann. "Electro-mechanical actuation modulates fracture performance of soft dielectric elastomers", International Journal of Engineering Science, vol.195, 104008. (2024). https://doi.org/10.1016/j.ijengsci.2023.104008Further explanation regarding the specimen preparation and experimental setup can be found in the aforementioned work.
This page was built for dataset: Fracture Dielectric Elastomers