Effects of the weak/micro-discontinuity of interface on the fracture behavior of a functionally graded coating with an inclined crack
From MaRDI portal
Recommendations
- Dynamic stress intensity factor of the weak/micro-discontinuous interface crack of a FGM coating
- Dynamic stress intensity factor of a crack perpendicular to the weak-discontinuous interface in a nonhomogeneous coating-substrate structure
- Fracture analysis of a functionally graded coating-substrate structure with a crack perpendicular to the interface. I: Static problem
- Fracture analysis of functionally graded coatings: antiplane deformation.
- Anti-plane transient fracture analysis of the functionally gradient elastic bi-material weak/infinitesimal-discontinuous interface
Cites work
- An anti-plane crack perpendicular to the weak/micro-discontinuous interface in a bi-FGM structure with exponential and linear non-homogeneities
- Anti-plane transient fracture analysis of the functionally gradient elastic bi-material weak/infinitesimal-discontinuous interface
- Bonded half planes containing an arbitrarily oriented crack
- Driving forces and kinking of an oblique crack in bonded nonhomogeneous materials
- Dynamic stress intensity factor of the weak/micro-discontinuous interface crack of a FGM coating
- Dynamic stress intensity factors of two collinear mode-III cracks perpendicular to and on the two sides of a bi-FGM weak-discontinuous interface
- Elastodynamic analysis of a crack at an arbitrary angle to the graded interfacial zone in bonded half-planes under antiplane shear impact
- Fracture analysis of a weak-discontinuous interface in a symmetrical functionally gradient composite strip loaded by anti-plane impact
- On the general treatment of an oblique crack near a bimaterial interface under antiplane loading
- On the numerical solution of singular integral equations
- Stress intensity factors for an oblique edge crack in a coating/substrate system with a graded interfacial zone under antiplane shear
- The general problem for an arbitrarily oriented crack in a FGM layer
- The mixed mode crack problem in an FGM layer bonded to a homogeneous half-plane
- The problem for bonded half-planes containing a crack at an arbitrary angle to the graded interfacial zone
- Two collinear interface cracks in magneto-electro-elastic composites
Cited in
(6)- Dynamic stress intensity factor of a crack perpendicular to the weak-discontinuous interface in a nonhomogeneous coating-substrate structure
- Fracture analysis on the arc-shaped interfacial crack between a homogeneous cylinder and its coating
- Dynamic stress intensity factor of the weak/micro-discontinuous interface crack of a FGM coating
- Fracture analysis of a nonhomogeneous coating/substrate system with an interface under thermal shock
- Anti-plane transient fracture analysis of the functionally gradient elastic bi-material weak/infinitesimal-discontinuous interface
- Analysis of anti-plane interface cracks in one-dimensional hexagonal quasicrystal coating
This page was built for publication: Effects of the weak/micro-discontinuity of interface on the fracture behavior of a functionally graded coating with an inclined crack
Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q1041471)