Initiation of fracture at the interface corner of bi-material joints.

DOI10.1016/S0022-5096(02)00076-5zbMath1100.74624OpenAlexW2003633835MaRDI QIDQ1811723

C. S. Meng, Alfred R. Akisanya

Publication date: 17 June 2003

Published in: Journal of the Mechanics and Physics of Solids (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1016/s0022-5096(02)00076-5

zbMATH Keywords

Stress intensity factorCorner singularitySmall-scale yieldingFailure criteriaBonded Joints

Mathematics Subject Classification ID

Singularities, blow-up, stress concentrations for dynamical problems in solid mechanics (74H35) Anelastic fracture and damage (74R20) Finite element methods applied to problems in solid mechanics (74S05)

Related Items (1)

Failure initiation in an epoxy joint between two steel plates

Cites Work

• Interfacial cracking from the free-edge of a long bi-material strip
• Connection between interface corner and interfacial fracture analyses of an adhesively-bonded butt joint
• Application of bimaterial interface corner failure mechanics to silicon/glass anodic bonds
• An application of two-state \(M\)-integral for computing the intensity of the singular near-tip field for a generic wedge
• Fracture initiation at three-dimensional bimaterial interface corners.
• The effect of corner angles in bimaterial structures

This page was built for publication: Initiation of fracture at the interface corner of bi-material joints.