Modeling of multiple crack initiation in polymer pipes under oxidative environment

DOI10.1016/J.IJENGSCI.2022.103686OpenAlexW4224237252MaRDI QIDQ2145223FDOQ2145223

Authors: Jung-Wook Wee, Alexander Chudnovsky, Byoung-Ho Choi 

Publication date: 17 June 2022

Published in: International Journal of Engineering Science (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1016/j.ijengsci.2022.103686

Recommendations

• Fracture initiation associated with chemical degradation: observation and modeling
• Mathematical modeling of growth of corrosion-mechanical cracks in oil pipeline taking into account hydro shocks and changes of characteristics of its material during operation
• Modeling of the process of corrosion cracking of underground pipelines
• A nonlinear and rate-dependent fracture phase field framework for multiple cracking of polymer
• Finite volume method and multigrid acceleration in modelling of rapid crack propagation in full-scale pipe test

zbMATH Keywords

Green's functionfracture energyoxygen diffusionmechanochemical degradationmultiple crack initiationpolymer pipe

Mathematics Subject Classification ID

Biology and other natural sciences (92-XX) Mechanics of deformable solids (74-XX)

Cites Work

• Fracture initiation associated with chemical degradation: observation and modeling
• Title not available (Why is that?)
• Slow crack growth, its modeling and crack-layer approach: a review
• Applying the crack-layer concept to modeling of slow crack growth in polyethylene

Cited In (3)

• On the mechanochemical dissolution of shells and its temperature dependence: discussion of different models
• Modeling of the process of corrosion cracking of underground pipelines
• Influence of material anisotropy on the mechanics of surface damage

This page was built for publication: Modeling of multiple crack initiation in polymer pipes under oxidative environment

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q2145223)