Modes I and II interlaminar fracture toughness and fatigue delamination of CF/epoxy laminates with self-same epoxy interleaf

DOI10.1016/J.IJFATIGUE.2006.02.004MaRDI QIDQ2506568zbMATH OpenOpenAlexFDO

Authors Masaki Hojo, Tadashi Ando, Mototsugu Tanaka, Taiji Adachi, Shojiro Ochiai, Yoshihiro Endo

Publication date 10 October 2006

Published in International Journal of Fatigue (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1016/j.ijfatigue.2006.02.004

zbMATH Keywords

delaminationfatigue crack growthmode Imode IIpolymer--matrix compositesself-same epoxy interleaf

Mathematics Subject Classification ID

Experimental work for problems pertaining to mechanics of deformable solids (74-05) Anelastic fracture and damage (74R20)

Recommendations

• Mode II fatigue crack growth from delamination in unidirectional tape and satin-woven fabric laminates of high strength GFRP
• Intralaminar fatigue behaviour of carbon fibre reinforced plastics
• Simulation and experimental validation of mixed mode delamination in multidirectional CF/PEEK laminates under fatigue loading
• Numerical evaluation of delamination on mode II in glass fiber reinforced composites
• Analysis of local delaminations in composite laminates with angle-ply matrix cracks.

Cited in

(2)

• Modeling arbitrarily oriented and reorienting multiscale cracks in composite materials with adaptive multiscale discrete damage theory
• Mode II fatigue crack growth from delamination in unidirectional tape and satin-woven fabric laminates of high strength GFRP

This page was built for publication: Modes I and II interlaminar fracture toughness and fatigue delamination of CF/epoxy laminates with self-same epoxy interleaf

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q2506568)