Research on the direction of fatigue crack propagation resulting from sharp concentrators of stress

DOI10.1023/B:FRAC.0000040961.28454.F1MaRDI QIDQ2519940zbMATH OpenOpenAlexFDO

Authors P. G. Surovin, V. M. Tikhomirov

Publication date 28 January 2009

Published in International Journal of Fracture (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1023/b:frac.0000040961.28454.f1

Mathematics Subject Classification ID

Experimental work for problems pertaining to mechanics of deformable solids (74-05) Fracture and damage (74R99)

Recommendations

• Experimental investigation on the propagation of fatigue cracks emanating from sharp notches
• Mechanisms of mixed mode fatigue crack propagation at rail butt-welds
• Kinetics of the fatigue failure of thin aluminum plates with cracks under asymmetric loading
• On the theory of growth of fatique mode I cracks in thin isotropic plates of finite size under uniaxial tension-compression
• Material plasticity dependence of mixed mode fatigue crack growth in commonly used engineering materials

Cited in

(6)

• scientific article; zbMATH DE number 1892996 (Why is no real title available?)
• A fatigue crack path analysis in rail weldment under mixed mode loading condition: a computational simulation
• Regularities of flat cracks growth in plates
• Mechanisms of mixed mode fatigue crack propagation at rail butt-welds
• Analysis of the effects of compressive stresses on fatigue crack propagation rate
• Experimental investigation on the propagation of fatigue cracks emanating from sharp notches

This page was built for publication: Research on the direction of fatigue crack propagation resulting from sharp concentrators of stress

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q2519940)