Mathematical models for estimation of residual life-time of plates with crack systems under the actions of long-term static loading, high temperature and hydrogen

DOI10.1007/S10958-015-2653-5MaRDI QIDQ2808387zbMATH OpenOpenAlexFDO

Authors O. Ye. Andrejkiv, N. V. Yavorska, V. Z. Kukhar

Publication date 23 May 2016

Published in Matematychni Metody ta Fizyko-Mekhanichni Polya (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1007/s10958-015-2653-5

zbMATH Keywords

energy approachlife-time of metal platesplate with system of cracks

Mathematics Subject Classification ID

Thermodynamics in solid mechanics (74A15) Theories of fracture and damage (74A45) Thermal effects in solid mechanics (74F05) Plates (74K20)

Recommendations

• Mathematical model of life-time determination for plates with systems of cracks under long-term static breaking load and high temperature
• Mathematical modeling of fracture processes in plates with crack systems subject to long-term loads, high temperature and corrosive medium
• Determination of durability of plates with crack systems under the action of long-term static tension and low-temperature field
• scientific article; zbMATH DE number 6177350
• A mathematical model for the determination of a period of subcritical propagation of high-temperature creep cracks in solids

Cites work

• A mathematical model for the determination of a period of subcritical propagation of high-temperature creep cracks in solids

Cited in

(7)

• A mathematical model for the determination of a period of subcritical propagation of high-temperature creep cracks in solids
• Mathematical model of life-time determination for plates with systems of cracks under long-term static breaking load and high temperature
• A calculation model for the determination of a period of the subcritical creep crack growth in structural elements under long-term static breaking loads
• Mathematical modeling of growth of corrosion-mechanical cracks in oil pipeline taking into account hydro shocks and changes of characteristics of its material during operation
• Mathematical modeling of fracture processes in plates with crack systems subject to long-term loads, high temperature and corrosive medium
• Determination of durability of plates with crack systems under the action of long-term static tension and low-temperature field
• A calculation model for the determination of subcritical crack growth periods in plates under block loading

This page was built for publication: Mathematical models for estimation of residual life-time of plates with crack systems under the actions of long-term static loading, high temperature and hydrogen

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q2808387)