Interface crack between two interface deformable piezoelectric layers

DOI10.1007/s10704-009-9359-yzbMath1273.74476OpenAlexW2052704081MaRDI QIDQ373417

Pizhong Qiao, Fangliang Chen

Publication date: 22 October 2013

Published in: International Journal of Fracture (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1007/s10704-009-9359-y

zbMATH Keywords

piezoelectric materialinterface fracturecrack energy density (CED)electromechanical loadingenergy release rate (ERR)interface deformable bi-layer beam theoryloading dependencepiezoelectric layered structures

Mathematics Subject Classification ID

Brittle fracture (74R10) Electromagnetic effects in solid mechanics (74F15)

Cites Work

• Interface crack between two shear deformable elastic layers
• Fracture mechanics for piezoelectric ceramics
• On the fracture mechanics of piezoelectric solids
• Interfacial cracks between piezoelectric and elastic materials under in-plane electric loading.
• On the crack-tip stress singularity of interfacial cracks in transversely isotropic piezoelectric bimaterials
• Exact solution for finite electrode layers embedded at the interface of two piezoelectric half-planes
• Analysis of beam-type fracture specimens with crack-tip deformation
• Switch-toughening of ferroelectrics subjected to electric fields
• Electric-field induced interfacial cracking in multilayer electrostrictive actuators
• Crack energy density and energy release rate for piezoelectric material
• Electroelastic field concentrations ahead of electrodes in multilayer piezoelectric actuators: experiment and finite element simulation
• Mechanics and fracture of crack tip deformable bi-material interface
• Crack Extension Force in a Piezoelectric Material
• Analysis of indentation cracking in piezoceramics
• Effect of local polarization switching on piezoelectric fracture

This page was built for publication: Interface crack between two interface deformable piezoelectric layers