Interface delamination of the thermal barrier coating subjected to local heating

DOI10.1007/S11431-010-4160-8MaRDI QIDQ546450zbMATH OpenOpenAlexFDO

Authors ChenWu Wu, ChenGuang Huang, Guangnan Chen

Publication date 24 June 2011

Published in Science China. Technological Sciences (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1007/s11431-010-4160-8

zbMATH Keywords

FE modelinginterface delaminationlocal heatingTBC

Mathematics Subject Classification ID

Thermal effects in solid mechanics (74F05) Finite element methods applied to problems in solid mechanics (74S05) Finite element, Galerkin and related methods applied to problems in thermodynamics and heat transfer (80M10)

Recommendations

• Parametric studies of failure mechanisms in elastic EB-PVD thermal barrier coatings using FEM
• Interfacial fracture characteristic and crack propagation of thermal barrier coatings under tensile conditions at elevated temperatures
• Effect of interface profile and stress-strain properties of substrate onto stability loss of thermal barrier coating under thermal impact
• Interfacial fracture toughness of APS bond coat/substrate under high temperature
• On debonding of graded thermal barrier coatings

Cites work

• A numerical study of turbulent combustion characteristics in a combustion chamber of a scramjet engine
• scientific article; zbMATH DE number 3155352 (Why is no real title available?)

Cited in

(6)

• Interfacial fracture characteristic and crack propagation of thermal barrier coatings under tensile conditions at elevated temperatures
• Interfacial fracture toughness of APS bond coat/substrate under high temperature
• Delamination of inhomogeneous coating
• Parametric studies of failure mechanisms in elastic EB-PVD thermal barrier coatings using FEM
• FAILURE ASSESSMENT OF UHTC PLATE UNDER ELEVATED TEMPERATURE
• Effect of interface profile and stress-strain properties of substrate onto stability loss of thermal barrier coating under thermal impact

This page was built for publication: Interface delamination of the thermal barrier coating subjected to local heating

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q546450)