The effect of crack blunting on the competition between dislocation nucleation and cleavage

DOI10.1016/S0022-5096(00)00042-9zbMath0991.74011OpenAlexW1992037469WikidataQ127662740 ScholiaQ127662740MaRDI QIDQ5930719

Lisa L. Fischer, Glenn E. Beltz

Publication date: 21 August 2002

Published in: Journal of the Mechanics and Physics of Solids (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1016/s0022-5096(00)00042-9

zbMATH Keywords

instabilityintegral equationatomic decohesionbrittle behaviourcleavagecontinuum mechanicscrap trip bluntingcritical energy release ratedislocation nucleationductile behaviouredge dislocationFrenkel formulalattice theorylocal slip displacementsiliconslender elliptical cracktwo-dimensional homogeneous isotropic linear elasticity

Mathematics Subject Classification ID

Brittle fracture (74R10) Micromechanical theories (74A60) Theories of fracture and damage (74A45)

Related Items (7)

Shielding effects of disclinations on the elliptical blunt crack ⋮ The stress intensity factor of an edge dislocation near an elliptically blunted crack tip ⋮ Effect of cooperative grain boundary sliding and migration on dislocation emitting from a semi-elliptical blunt crack tip in nanocrystalline solids ⋮ A theoretical modelling of strengthening mechanism in graphene-metal nanolayered composites ⋮ Interaction of a screw dislocation with a parabolic cavity and a semi-infinite crack ⋮ A finite Zener-Stroh crack interacting with a blunt crack under in-plane deformations ⋮ Dislocation emission criterion from a blunt crack tip

Cites Work

• Unnamed Item
• Yielding from a crack with finite root-radius loaded in uniform tension
• The formation of equilibrium cracks during brittle fracture. General ideas and hypotheses. Axially-symmetric cracks
• VI. The phenomena of rupture and flow in solids

This page was built for publication: The effect of crack blunting on the competition between dislocation nucleation and cleavage