A chemo-thermo-mechanical coupled phase field framework for failure in thermal barrier coatings
From MaRDI portal
(Redirected from Publication:6097589)
Recommendations
- Dual-horizon peridynamics modeling of coupled chemo-mechanical-damage for interface oxidation-induced cracking in thermal barrier coatings
- Coupled diffusion-viscoplasticity-phase field modeling for calcia-magnesia-alumina-silicate (CMAS) corrosion assisted fracture of thermal barrier coating system
- A life prediction model of thermal barrier coatings
- Parametric studies of failure mechanisms in elastic EB-PVD thermal barrier coatings using FEM
- A chemo-thermo-mechanically coupled theory for elastic-viscoplastic deformation, diffusion, and volumetric swelling due to a chemical reaction
Cites work
- A ductile phase-field model based on degrading the fracture toughness: theory and implementation at small strain
- A phase field model for cohesive fracture in micropolar continua
- A phase field model for rate-independent crack propagation: robust algorithmic implementation based on operator splits
- A phase-field description of dynamic brittle fracture
- A phase-field formulation for dynamic cohesive fracture
- A review on phase-field models of brittle fracture and a new fast hybrid formulation
- An accelerated staggered scheme for variational phase-field models of brittle fracture
- An efficient and robust monolithic approach to phase-field quasi-static brittle fracture using a modified Newton method
- An efficient and robust staggered algorithm applied to the quasi-static description of brittle fracture by a phase-field approach
- An open-source Abaqus implementation of the phase-field method to study the effect of plasticity on the instantaneous fracture toughness in dynamic crack propagation
- Crack kinking in a variational phase-field model of brittle fracture with strongly anisotropic surface energy
- Generalized Ginzburg-Landau and Cahn-Hilliard equations based on a microforce balance
- Interior-point methods for the phase-field approach to brittle and ductile fracture
- Mapped phase field method for brittle fracture
- Modified Newton methods for solving fully monolithic phase-field quasi-static brittle fracture propagation
- Multi-phase-field modeling of anisotropic crack propagation for polycrystalline materials
- Nonlocal operator method for dynamic brittle fracture based on an explicit phase field model
- Numerical experiments in revisited brittle fracture
- On realizing specific failure initiation criteria in the phase field model
- Phase field approximation of cohesive fracture models
- Phase field modeling of fracture in quasi-brittle materials using natural neighbor Galerkin method
- Phase-field modeling of ductile fracture
- Phase-field modelling of cohesive fracture
- Phase-field modelling of interface failure in brittle materials
- Phase-field simulation of ductile fracture in shell structures
- Revisiting brittle fracture as an energy minimization problem
- Revisiting the problem of a crack impinging on an interface: a modeling framework for the interaction between the phase field approach for brittle fracture and the interface cohesive zone model
- The variational approach to fracture
- Thermodynamically consistent phase-field models of fracture: variational principles and multi-field FE implementations
- Transient thermal and thermomechanical analysis by mixed FEM
- Variational phase-field fracture modeling with interfaces
Cited in
(10)- Dual-horizon peridynamics modeling of coupled chemo-mechanical-damage for interface oxidation-induced cracking in thermal barrier coatings
- Finite element simulations of the thermomechanically coupled responses of thermal barrier coating systems using an unconditionally stable staggered approach
- A thermo-mechanical localizing gradient damage model with modified Mazars strain
- Model-free chemomechanical interfaces: history-dependent damage under transient mass diffusion
- The fully coupled thermo-mechanical dual-horizon peridynamic correspondence damage model for homogeneous and heterogeneous materials
- A novel semi-explicit numerical algorithm for efficient 3D phase field modelling of quasi-brittle fracture
- Analysis of crack nets development in thermal barrier coatings
- Modelling high temperature progressive failure in C/SiC composites using a phase field model: oxidation rate controlled process
- Staggered algorithms for coupled problems: convergence analysis and application to phase field modeling of thermal cracking
- Dynamic fracture investigation of concrete by a rate-dependent explicit phase field model integrating viscoelasticity and micro-viscosity
This page was built for publication: A chemo-thermo-mechanical coupled phase field framework for failure in thermal barrier coatings
Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q6097589)