Mode I crack propagation in an elastic layer is discussed, where the crack edge travels at sub-Rayleigh velocity with respect to the layer and supersonic velocity with respect to outer medium. The theoretical basis for expecting the plane stress Rayleigh wave velocity of the outer medium as an upper limit of the crack velocity in experiments is discussed.
Recommendations
Cited in
(15)- Transition of mode II cracks from sub-Rayleigh to intersonic speeds in the presence of favorable heterogeneity
- Dynamic crack growth in TDCB specimens
- Instability of critical characteristics of crack propagation
- Macroscopic and microscopic examination of the relationship between crack velocity and path and Rayleigh surface wave speed in single crystal silicon
- Damage and cracking in thin mud layers
- Limiting velocity of crack propagation in elastic materials
- Dynamic crack growth under Rayleigh wave
- Dynamic crack propagation based on loss of hyperbolicity and a new discontinuous enrichment
- Limiting velocity of crack propagation in dynamically fractured materials
- scientific article; zbMATH DE number 858427 (Why is no real title available?)
- scientific article; zbMATH DE number 7492820 (Why is no real title available?)
- Sub-Rayleigh to supershear transition of dynamic mode-II cracks
- Moving line crack accompanied with damage zone subject to remote tensile loading
- Modern topics and challenges in dynamic fracture
- When and how do cracks propagate?
This page was built for publication: Dynamic crack propagation in a layer
Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q675427)