The crack growth resistance of thin steel sheets under eccentric tension

DOI10.1007/S12046-018-0785-2MaRDI QIDQ724667zbMATH OpenOpenAlexFDO

Authors L'. Ambriško, Luděk Pešek

Publication date 26 July 2018

Published in Sādhanā (Search for Journal in Brave)

Full work available at URL https://www.ias.ac.in/describe/article/sadh/043/02/0025

zbMATH Keywords

cold-formed steelR-curvestable crack growththin sheetvideoextensometry

Mathematics Subject Classification ID

Brittle fracture (74R10)

Recommendations

• Effect of thickness on fracture criterion in general yielding fracture mechanics
• Further developments in \(J\) evaluation procedure for growing cracks based on LLD and CMOD data
• Material plasticity dependence of mixed mode fatigue crack growth in commonly used engineering materials
• Experimental results and predictions on fatigue crack growth in structural steel
• Relation between fatigue crack initiation and propagation, toughness and microstructure in large steel blooms for automotive plastic molds

Cites work

• \(J\)-integral resistance curve testing and evaluation
• scientific article; zbMATH DE number 4147659 (Why is no real title available?)
• scientific article; zbMATH DE number 1047380 (Why is no real title available?)
• Relationships between the J-integral and the crack opening displacement for stationary and extending cracks

Cited in

(5)

• Effect of thickness on fracture criterion in general yielding fracture mechanics
• Transient stress effects on fatigue crack growth thresholds due to testing methodology
• Development of testing systems for dynamic assessment of sheet metal specimens
• Analysis of crack formation in T-joint structures under dynamic loading
• Fatigue crack growth behavior in ferritic - pearlitic steels with networked and distributed pearlite structures

This page was built for publication: The crack growth resistance of thin steel sheets under eccentric tension

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q724667)