Nonlinear fracture mechanics of flexural-shear crack induced debonding of FRP strengthened concrete beams

DOI10.1016/J.IJSOLSTR.2008.01.004MaRDI QIDQ837277zbMATH OpenOpenAlexFDO

Authors Jialai Wang, Chao Zhang

Publication date 10 September 2009

Published in International Journal of Solids and Structures (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1016/j.ijsolstr.2008.01.004

zbMATH Keywords

cohesive zone modelconcretedebondingfiber reinforced polymerflexural-shear crackintermediate crack induced debondingmixed-modestrengthening

Mathematics Subject Classification ID

Composite and mixture properties (74E30) Explicit solutions of equilibrium problems in solid mechanics (74G05) Fracture and damage (74R99) Finite element methods applied to problems in solid mechanics (74S05)

Recommendations

• Cohesive zone model of FRP-concrete interface debonding under mixed-mode loading
• Debonding of frp-plated reinforced concrete beam, a bond-slip analysis. I: Theoretical formulation
• Cohesive zone model of intermediate crack-induced debonding of FRP-plated concrete beam
• Debonding analysis of FRP-concrete interface between two balanced adjacent flexural cracks in plated beams
• FRP-to-concrete interfaces between two adjacent cracks: theoretical model for debonding failure

Cites work

• Analysis of beam-type fracture specimens with crack-tip deformation
• Analytical methods in rotor dynamics
• Cohesive zone model of FRP-concrete interface debonding under mixed-mode loading
• Cohesive zone model of intermediate crack-induced debonding of FRP-plated concrete beam
• Debonding of frp-plated reinforced concrete beam, a bond-slip analysis. I: Theoretical formulation
• Interface crack between two shear deformable elastic layers
• Mixed Mode Cracking in Layered Materials

Cited in

(16)

• Dynamic edge debonding in FRP strengthened beams
• A coupled interface-body nonlocal damage model for FRP strengthening detachment
• Fracture resistance of a cracked concrete beam post-strengthened with FRP sheets
• Analyzing the bond behavior of fiber-reinforced polymer (FRP) bars embedded in engineered cementitious composites (ECCs) with the nonlocal continuum rod model
• Fracture mechanical analysis of strengthened concrete tension members with one crack
• Cohesive zone model of FRP-concrete interface debonding under mixed-mode loading
• FRP-to-concrete interfaces between two adjacent cracks: theoretical model for debonding failure
• Cohesive zone model of intermediate crack-induced debonding of FRP-plated concrete beam
• Debonding of frp-plated reinforced concrete beam, a bond-slip analysis. I: Theoretical formulation
• Non-linear fracture study of single cantilever beam specimen
• Nonlinear finite element analysis of FRP strengthened RC beams with bond-slip effect
• Impact of thermal loads on interfacial debonding in FRP strengthened beams
• Interfacial stresses in strengthened beam with shear cohesive zone model
• Modeling of mixed-mode debonding in the peel test applied to superficial reinforcements
• Debonding analysis of FRP-concrete interface between two balanced adjacent flexural cracks in plated beams
• A three-parameter elastic foundation model for interface stresses in curved beams externally strengthened by a thin FRP plate

This page was built for publication: Nonlinear fracture mechanics of flexural-shear crack induced debonding of FRP strengthened concrete beams

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q837277)