Surfaces formed by subcritical crack growth in silicate glasses

DOI10.1007/S10704-006-6729-6zbMATH Open1342.74150OpenAlexW1996363288MaRDI QIDQ865249FDOQ865249

S. M. Wiederhorn, J. P. Guin

Publication date: 13 February 2007

Published in: International Journal of Fracture (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1007/s10704-006-6729-6

zbMATH Keywords

fractureatomic force microscopycavitationsubcritical crack growthglass

Mathematics Subject Classification ID

Statistical mechanics of random media, disordered materials (including liquid crystals and spin glasses) (82D30) Fracture and damage (74R99)

Cites Work

• The penetration of a fluid into a porous medium or Hele-Shaw cell containing a more viscous liquid
• Nano-ductile crack propagation in glasses under stress corrosion: spatiotemporal evolution of damage in the vicinity of the crack tip

Cited In (2)

• Self-emitted surface corrugations in dynamic fracture of silicon single crystal
• Nano-ductile crack propagation in glasses under stress corrosion: spatiotemporal evolution of damage in the vicinity of the crack tip

   Recommendations

• Nanoscale damage during fracture in silica glass 👍 👎
• Nano-ductile crack propagation in glasses under stress corrosion: spatiotemporal evolution of damage in the vicinity of the crack tip 👍 👎
• On dynamic surface instabilities of cracks in brittle crystals 👍 👎
• Microscopic aspects of crack propagation along PET--glass and PET--Al interfaces 👍 👎
• Crack Initiation, Kinking and Nanoscale Damage in Silica Glass: Multimillion-Atom Molecular Dynamics Simulations 👍 👎

This page was built for publication: Surfaces formed by subcritical crack growth in silicate glasses

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q865249)