Determination of mode II fracture toughness for U-shaped notches using Brazilian disc specimen
From MaRDI portal
Publication:960774
DOI10.1016/J.IJSOLSTR.2009.10.012zbMath1183.74231OpenAlexW2046657012MaRDI QIDQ960774
A. R. Torabi, Majid R. Ayatollahi
Publication date: 29 March 2010
Published in: International Journal of Solids and Structures (Search for Journal in Brave)
Full work available at URL: https://doi.org/10.1016/j.ijsolstr.2009.10.012
Brittle fracture (74R10) Finite element methods applied to problems in solid mechanics (74S05) Experimental work for problems pertaining to mechanics of deformable solids (74-05)
Related Items (1)
Cites Work
- Mixed mode failure criteria for brittle elastic V-notched structures
- Local strain energy to assess the static failure of U-notches in plates under mixed mode loading
- Failure criteria for linear elastic materials with U-notches
- A failure criterion for brittle elastic materials under mixed-mode loading
- Mixed mode fracture in soda lime glass analyzed by using the generalized MTS criterion
- Failure criteria for brittle elastic materials
- A fracture criterion for blunted V-notched samples
- Fracture initiation at sharp notches: Correlation using critical stress intensities
- Strength or toughness? A criterion for crack onset at a notch
- Developments of some explicit formulas useful to describe elastic stress fields ahead of notches in plates.
- Fracture assessment of U-notches under mixed mode loading: two procedures based on the `equivalent local mode I' concept
- Investigation of failure criteria for a sharp notch
- A generalized stress intensity factor to be applied to rounded V-shaped notches
- On determination of mode II fracture toughness using semi-circular bend specimen
- On the consequences of T-stress in elastic brittle fracture
- A criterion for crack nucleation at a notch in homogeneous materials
This page was built for publication: Determination of mode II fracture toughness for U-shaped notches using Brazilian disc specimen