Effects of applied stress level on plastic zone size and opening stress ratio of a fatigue crack

DOI10.1016/J.IJFATIGUE.2004.09.008zbMATH Open1194.74324OpenAlexW2072921086MaRDI QIDQ993965FDOQ993965

Authors: Guoqiang Li, Juan Hou, Tien-Chong Chang 

Publication date: 16 September 2010

Published in: International Journal of Fatigue (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1016/j.ijfatigue.2004.09.008

Recommendations

• A reexamination of plasticity-induced crack closure in fatigue crack propagation
• Fatigue Crack Closure Following a Step-Increase Load
• Analysis of the effects of compressive stresses on fatigue crack propagation rate
• A comparison of two and three-dimensional analyses of fatigue crack closure
• Fracture mechanics analysis for residual stress and crack closure corrections

zbMATH Keywords

fatigue crack closureopening stressreversed plastic zonestress level

Mathematics Subject Classification ID

Anelastic fracture and damage (74R20) Complex-variable methods applied to problems in solid mechanics (74S70)

Cited In (3)

• A reexamination of plasticity-induced crack closure in fatigue crack propagation
• Fracture mechanics analysis for residual stress and crack closure corrections
• The distributed dislocation technique for calculating plasticity-induced crack closure in plates of finite thickness

This page was built for publication: Effects of applied stress level on plastic zone size and opening stress ratio of a fatigue crack

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q993965)