The collinear crack problem for an orthotropic functionally graded coating-substrate structure
From MaRDI portal
Recommendations
- Anti-plane problem of two collinear cracks in a functionally graded coating-substrate structure
- Mode I crack problem for a functionally graded orthotropic coating-substrate structure
- Mode-I crack problem for functionally graded layered structures
- Anti-plane problem of periodic interface cracks in a functionally graded coating-substrate structure
- Mode I crack problem for a functionally graded orthotropic strip
Cites work
- Analysis of a mode III crack problem in a functionally graded coating-substrate system with finite thickness
- Dynamic stress intensity factor of the weak/micro-discontinuous interface crack of a FGM coating
- Dynamic stress intensity factors of two collinear mode-III cracks perpendicular to and on the two sides of a bi-FGM weak-discontinuous interface
- Fracture analysis of a functionally graded interfacial zone under plane deformation
- scientific article; zbMATH DE number 3387263 (Why is no real title available?)
- scientific article; zbMATH DE number 3081975 (Why is no real title available?)
- Mode I crack problem for a functionally graded orthotropic strip
- On some crack problems for inhomogeneous elastic materials
- Periodic Antiplane Cracks in Graded Coatings Under Static or Transient Loading
- The collinear cracks in an inhomogeneous medium subjected to transient load
- The dynamic response of an edge crack in a functionally graded orthotropic strip
- The Mode III Crack Problem in Bonded Materials With a Nonhomogeneous Interfacial Zone
- Transient response of a mode III crack in an orthotropic functionally graded strip
Cited in
(14)- Analytic solutions of multiple moving cracks in an orthotropic layer bonded to an orthotropic FGM coating
- Elastodynamic response of symmetric edge cracks in an orthotropic strip
- Interface crack at orthotropic media
- Mode-I crack problem for functionally graded layered structures
- Mode I crack problem for a functionally graded orthotropic coating-substrate structure
- Anti-plane problem of periodic interface cracks in a functionally graded coating-substrate structure
- Anti-plane problem of two collinear cracks in a functionally graded coating-substrate structure
- Non-Fourier thermoelastic interaction of two collinear cracks in a functionally graded layer
- An application of Lobatto–Chebyshev method to a nonhomogeneous plane problem with two cracks
- Dynamic analysis of interfacial multiple cracks in piezoelectric thin film/substrate
- Analysis of a mode III crack problem in a functionally graded coating-substrate system with finite thickness
- Size effect on the thermal fracture behavior of collinear interface cracks in functionally graded coating/substrate structures
- Analysis of an orthotropic strip containing multiple defects bonded between two piezoelectric layers
- A partially insulated interface crack between a graded orthotropic coating and a homogeneous orthotropic substrate under heat flux supply
This page was built for publication: The collinear crack problem for an orthotropic functionally graded coating-substrate structure
Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q2511610)