A void-crack nucleation model for ductile metals
From MaRDI portal
Publication:1302790
DOI10.1016/S0020-7683(98)00239-XzbMath0941.74051OpenAlexW2104384632WikidataQ126550870 ScholiaQ126550870MaRDI QIDQ1302790
Mark F. Horstemeyer, Arun M. Gokhale
Publication date: 22 September 1999
Published in: International Journal of Solids and Structures (Search for Journal in Brave)
Full work available at URL: https://doi.org/10.1016/s0020-7683(98)00239-x
volume fractionfracture toughnessductile metalslength scale parameterAl-Si-Mg alloyphenomenological void-crack nucleation modelsecond phase
Anelastic fracture and damage (74R20) Experimental work for problems pertaining to mechanics of deformable solids (74-05)
Related Items (5)
Calibration, validation, and verification including uncertainty of a physically motivated internal state variable plasticity and damage model ⋮ Historical review of internal state variable theory for inelasticity ⋮ Modeling strength and failure variability due to porosity in additively manufactured metals ⋮ Micromechanisms of ductile fracturing of DH-36 steel plates under impulsive loads and influence of polyurea reinforcing ⋮ A multiphase internal state variable model with rate equations for predicting elastothermoviscoplasticity and damage of fiber-reinforced polymer composites