Growth of interfacial cracks in a TBC/superalloy system due to oxide volume induced internal pressure and thermal loading.
From MaRDI portal
DOI10.1016/S0020-7683(98)00321-7zbMATH Open1090.74662MaRDI QIDQ1573576FDOQ1573576
Authors: S. Q. Nusier, G. M. Newaz 
Publication date: 2000
Published in: International Journal of Solids and Structures (Search for Journal in Brave)
Recommendations
- An analytical model of rumpling in thermal barrier coatings
- Coupled effects of temperature gradient and oxidation on thermal stress in thermal barrier coating system
- Interfacial fracture characteristic and crack propagation of thermal barrier coatings under tensile conditions at elevated temperatures
- On debonding of graded thermal barrier coatings
- Analysis of crack nets development in thermal barrier coatings
Thermal effects in solid mechanics (74F05) Brittle fracture (74R10) Finite element methods applied to problems in solid mechanics (74S05)
Cited In (12)
- Coupled effects of temperature gradient and oxidation on thermal stress in thermal barrier coating system
- A chemo-thermo-mechanically coupled theory for elastic-viscoplastic deformation, diffusion, and volumetric swelling due to a chemical reaction
- A simple model for the study of the tolerance of interfacial crack under thermal load
- Numerical simulation of the spallation of a thermal barrier coating. Coupling between oxydation and mechanical behaviour.
- Interfacial fracture characteristic and crack propagation of thermal barrier coatings under tensile conditions at elevated temperatures
- Fatigue cracks in a thermal barrier coating system on a superalloy in multiaxial thermomechanical testing
- A fundamental model of cyclic instabilities in thermal barrier systems
- Boundary element analysis of cracked homogeneous or bi-material structures under thermo-mechanical cycling
- Etude des propriétés thermomécaniques et du phénomène de fissuration périodique des films d'oxyde à haute température
- On debonding of graded thermal barrier coatings
- Effect of interface profile and stress-strain properties of substrate onto stability loss of thermal barrier coating under thermal impact
- An analytical model of rumpling in thermal barrier coatings
This page was built for publication: Growth of interfacial cracks in a TBC/superalloy system due to oxide volume induced internal pressure and thermal loading.
Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q1573576)