Stress-based criteria for brittle fracture in key-hole notches under mixed mode loading

DOI10.1016/J.EUROMECHSOL.2014.06.009MaRDI QIDQ1669484zbMATHOpenAlexFDO

Authors A. R. Torabi, E. Pirhadi

Publication date 3 September 2018

Published in European Journal of Mechanics. A. Solids (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1016/j.euromechsol.2014.06.009

zbMATH Keywords

mixed mode loadingbrittle fracturekey-hole notch

Mathematics Subject Classification ID

Brittle fracture (74R10)

Recommendations

• Limit curves for brittle fracture in key-hole notches under mixed mode I/III loading based on stress-based criteria
• Combined tension-shear fracture analysis of V-notches with end holes
• Fracture assessment of U-notches under mixed mode loading: two procedures based on the `equivalent local mode I' concept
• Mixed mode failure criteria for brittle elastic V-notched structures
• Compressive brittle fracture in V-notches with end holes

Cites work

• A failure criterion for brittle elastic materials under mixed-mode loading
• An implicit gradient type of static failure criterion for mixed-mode loading
• Calculation of the energy \(J\)-integral for bodies with notches and cracks
• Failure criteria for brittle elastic materials
• Failure initiation at a blunt V-notch tip under mixed mode loading
• In-plane and out-of-plane stress field solutions for V-notches with end holes
• Influence of the root radius of crack-like notches on the fracture load of brittle components
• Investigation of failure criteria for a sharp notch
• Local strain energy to assess the static failure of U-notches in plates under mixed mode loading
• Relationships between \(J\)-integral and the strain energy evaluated in a finite volume surrounding the tip of sharp and blunt V-notches

Cited in

(10)

• Fracture assessment of U-notches under mixed mode loading: two procedures based on the `equivalent local mode I' concept
• Mixed mode fracture in soda lime glass analyzed by using the generalized MTS criterion
• Compressive brittle fracture in V-notches with end holes
• Combined tension-shear fracture analysis of V-notches with end holes
• Two-parameter fracture criterion \((K_{\rho,c}-T_{ef,c})\) based on notch fracture mechanics
• Limit curves for brittle fracture in key-hole notches under mixed mode I/III loading based on stress-based criteria
• The circumferential stress-strain product criterion of mixed mode brittle fracture
• The effects of different boundary conditions on three-dimensional cracked discs under anti-plane loading
• The brittle fracture criterion based on the maximum tensile stress on the surface of blunt crack tip
• Determination of mode II fracture toughness for U-shaped notches using Brazilian disc specimen

This page was built for publication: Stress-based criteria for brittle fracture in key-hole notches under mixed mode loading

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q1669484)