Thermomechanical fracture behaviour of interacting microdefects in thermal barrier coatings

DOI10.1007/S00707-022-03228-0MaRDI QIDQ2156229zbMATH OpenOpenAlexFDO

Authors L. Y. Lim, S. A. Meguid

Publication date 18 July 2022

Published in Acta Mechanica (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1007/s00707-022-03228-0

zbMATH Keywords

finite element modelstress intensity factoradaptive remeshing algorithmautomatic geometry reconstructioncrack tracking criteriondominant crackthermal stress effect

Mathematics Subject Classification ID

Thermal effects in solid mechanics (74F05) Micromechanics of solids (74M25) Brittle fracture (74R10) Finite element methods applied to problems in solid mechanics (74S05) Stress concentrations, singularities in solid mechanics (74G70)

Recommendations

• Interfacial fracture characteristic and crack propagation of thermal barrier coatings under tensile conditions at elevated temperatures
• A life prediction model of thermal barrier coatings
• Fracture mechanical damage modelling of thermal barrier coatings
• Analysis of crack nets development in thermal barrier coatings
• Micromechanical analysis of failure in thin protective coatings

Cites work

• A self-consistent mechanics method for solids containing inclusions and a general distribution of cracks
• A strain energy-based parameter for predicting the crack initiation angle of mixed mode fracture
• An approximate scheme for considering effects of microcrack interaction on the overall constitutive relation of brittle solids under complex loading
• General solution to the problem of microcracks near the tip of a main crack
• On crack perturbation in thermoelastic media
• X-Fem analysis of the effects of holes or other cracks on dynamic crack propagations

Cited in

(10)

• A multi-scale constitutive model for the sintering of an air-plasma-sprayed thermal barrier coating, and its response under hot isostatic pressing
• Non-Fourier thermoelastic interaction of two collinear cracks in a functionally graded layer
• Analysis of the spallation mechanism suppression in plasma-sprayed TBCs through the use of heterogeneous bond coat architectures
• Interfacial fracture characteristic and crack propagation of thermal barrier coatings under tensile conditions at elevated temperatures
• Thermal-mechanical interface crack behaviour of a surface mount solder joint
• Micromechanical theoretical and computational modeling of energy dissipation due to nonlinear vibration of hard ceramic coatings with microstructural recursive faults
• Analytical solution of the thermoelastic problem of the asymmetric collinear nano-cracks in one-dimensional hexagonal quasicrystals
• Analysis of crack nets development in thermal barrier coatings
• Numerical approach to microstructural characterizations for dense and porous thermal barrier coatings
• Micromechanical analysis of failure in thin protective coatings

This page was built for publication: Thermomechanical fracture behaviour of interacting microdefects in thermal barrier coatings

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q2156229)