Fatigue behavior of CFRP cross-ply laminates under on-axis and off-axis cyclic loading

DOI10.1016/J.IJFATIGUE.2006.02.011MaRDI QIDQ2506593zbMATH OpenOpenAlexFDO

Authors Keiichiro Tohgo, Shuji Nakagawa, Kazuro Kageyama

Publication date 10 October 2006

Published in International Journal of Fatigue (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1016/j.ijfatigue.2006.02.011

zbMATH Keywords

\(S\)--\(N\) curveCFRP cross-ply laminatesfatigue behaviorfiber-peeling damageply-cracking damagetensile properties

Mathematics Subject Classification ID

Experimental work for problems pertaining to mechanics of deformable solids (74-05) Anelastic fracture and damage (74R20)

Recommendations

• Fatigue characteristics of quasi-isotropic CFRP laminates subjected to variable amplitude cyclic two-stage loading
• Fatigue strengths of cross-ply cfrp laminates at room and high temperatures and its phenomenological modeling
• Intralaminar fatigue behaviour of carbon fibre reinforced plastics
• A progressive first ply failure model for woven ply CFRP laminates under static and fatigue loads
• Accumulation of microdamages during cyclic loading of CFRP structure elements
• Cyclic fatigue behavior of carbon fiber reinforced vinylester resin composites manufactured by RTM and VARI
• A damage meso-mechanical approach to fatigue failure prediction of cross-ply laminate composites
• Prediction of long-term fatigue life of quasi-isotropic CFRP laminates for aircraft use
• Correlation of statistical fatigue properties in a wide stress range for FRP laminates with failure mechanisms
• Numerical simulation of interlaminar damage propagation in CFRP cross-ply laminates under transverse loading

Cited in

(13)

• A damage meso-mechanical approach to fatigue failure prediction of cross-ply laminate composites
• Correlation of statistical fatigue properties in a wide stress range for FRP laminates with failure mechanisms
• Mode II fatigue crack growth from delamination in unidirectional tape and satin-woven fabric laminates of high strength GFRP
• Intralaminar fatigue behaviour of carbon fibre reinforced plastics
• Damage mechanisms induced by cyclic ply-stresses in carbon--epoxy laminates: environmental effects
• Effects of \(R\)-ratio on the off-axis fatigue behavior of unidirectional hybrid GFRP/Al laminates at room temperature
• Fatigue crack constraint in plain-woven CFRP using newly-developed spread tows
• Cyclic fatigue behavior of carbon fiber reinforced vinylester resin composites manufactured by RTM and VARI
• Characterisation of the tensile fatigue behaviour of RTM-laminates by isocyclic stress--strain-diagrams
• Fatigue characteristics of quasi-isotropic CFRP laminates subjected to variable amplitude cyclic two-stage loading
• Effect of temperature and after-cure on fatigue fracture behavior of a glass/phenol composite
• Fatigue strengths of cross-ply cfrp laminates at room and high temperatures and its phenomenological modeling
• Infrared thermographic techniques for non-destructive damage characterization of carbon fibre reinforced polymers during tensile fatigue testing

This page was built for publication: Fatigue behavior of CFRP cross-ply laminates under on-axis and off-axis cyclic loading

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q2506593)