Effect of interfacial delamination on coating crack in thick diamond-like carbon coatings under indentation
From MaRDI portal
Publication:2699332
DOI10.1007/s10409-020-00930-xOpenAlexW3009082710MaRDI QIDQ2699332
Jun Luo, Xiangli Zhong, Fugang Qi, Xiaoping Ouyang, Bin Liao, Zhong-Bao Wang, Limei Jiang, Jinbin Wang
Publication date: 26 April 2023
Published in: Acta Mechanica Sinica (Search for Journal in Brave)
Full work available at URL: https://doi.org/10.1007/s10409-020-00930-x
Cites Work
- Dynamic crack propagation analysis of orthotropic media by the extended finite element method
- A theoretical and numerical study of thin film delamination using the pull-off test
- X-FEM a good candidate for energy conservation in simulation of brittle dynamic crack propagation
- Two-dimensional analysis of progressive delamination in thin film electrodes
- Micromechanics of substrate-supported thin films
- Determination of stress intensity factor with direct stress approach using finite element analysis
- 3D crack propagation with cohesive elements in the extended finite element method
- Mixed Mode Cracking in Layered Materials
- Extended finite element method for three-dimensional crack modelling
- A finite element method for crack growth without remeshing
This page was built for publication: Effect of interfacial delamination on coating crack in thick diamond-like carbon coatings under indentation