The Interface Crack Under Combined Loading

DOI10.1115/1.3125833zbMath0671.73074OpenAlexW1992191240MaRDI QIDQ3823900

John Dundurs, A. K. Gautesen

Publication date: 1988

Published in: Journal of Applied Mechanics (Search for Journal in Brave)

Full work available at URL: https://doi.org/10.1115/1.3125833

zbMATH Keywords

equationcombined tension-compression and shear loadingexactly solved governing integral

Mathematics Subject Classification ID

Stress concentrations, singularities in solid mechanics (74G70) Brittle damage (74R05) Singular integral equations (45E99)

Related Items

An analytically-numerical approach for the analysis of an interface crack with a contact zone in a piezoelectric bimaterial compound ⋮ The displacement field due to an interface crack along an elastic inclusion in a differing elastic matrix ⋮ An interface crack between elastic materials when there is dry friction ⋮ An interface crack with contact zones in a piezoelectric/piezomagnetic bimaterial ⋮ Analysis of stress intensity factors for three-dimensional interface crack problems in electronic packages using the virtual crack closure technique ⋮ An electroded electrically and magnetically charged interface crack in a piezoelectric/piezomagnetic bimaterial ⋮ Fracture behavior of periodically bonded interface of piezoelectric bi-material under compressive–shear loading ⋮ The sliding interface crack with friction between elastic and rigid bodies ⋮ Interface cracks in anisotropic dissimilar materials: An analytic solution ⋮ Determination of higher-order terms in asymptotic elastoplastic crack tip solutions ⋮ Propagating interface cracks with frictionless contact ⋮ Influence of concentrated loading on opening of an interface crack between piezoelectric materials in a compressive field ⋮ Investigation of the Process Zone Near the Tip of an Interface Crack in the Elastic Body in Shear Within the Framework of the Complex Model ⋮ Influence of the Lateral Process Zone Near the Tip of an Interface Crack on the Contact of its Faces ⋮ Stress state characterization of delamination cracks in [0/90 symmetric laminates by BEM] ⋮ Contact zone models for an interface crack in a piezoelectric material ⋮ Boundary element analysis of the stress intensity factors of plane interface cracks between dissimilarly adjoined anisotropic materials ⋮ Investigation of the behavior of a Griffith crack at the interface between two dissimilar orthotropic elastic half-planes for the opening crack mode ⋮ Crack kinking from an interface crack with initial contact between the crack lips