scientific article; zbMATH DE number 1302780

MaRDI QIDQ4249249zbMATHFDO

Authors K. M. Nikbin

Publication date 27 January 2000

zbMATH Keywords

defectscyclic loadingcrack initiationstatic loadingcreep uniaxial ductilityengineering creep parametershigh-temperature life-assessment methods

Mathematics Subject Classification ID

Thermal effects in solid mechanics (74F05) Anelastic fracture and damage (74R20) Research exposition (monographs, survey articles) pertaining to mechanics of deformable solids (74-02)

Recommendations

• The influence of high-temperature creep on the start of a fatigue crack in solids near stress concentrators
• Ductile fracture and lifetime prediction of structural materials and components under high-temperature creep conditions
• scientific article; zbMATH DE number 1047380
• An analogue of the Griffith problem for the propagation of creep-fatigue cracks
• scientific article; zbMATH DE number 1634829

Cited in

(9)

• A methodology for predicting creep/fatigue crack growth rates in Ti 6246
• Creep crack growth modelling of Grade 91 vessel weldments using a modified ductility based damage model
• An analogue of the Griffith problem for the propagation of creep-fatigue cracks
• The influence of high-temperature creep on the start of a fatigue crack in solids near stress concentrators
• Fatigue resistance at variation of temperature-time factors
• Ductile fracture and lifetime prediction of structural materials and components under high-temperature creep conditions
• Fatigue - creep behavior of 1.25Cr0.5Mo steel at high temperature and its life prediction
• Engineering application of enhanced \(C^*\)-\(Q^*\) two parameter approaches for predicting creep crack initiation times
• Study of fatigue crack growth in strain-hardening materials during creep

This page was built for publication:

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q4249249)