Mixed mode failure criteria for brittle elastic V-notched structures

DOI10.1007/S10704-007-9098-XzbMATH Open1198.76139OpenAlexW2032095117MaRDI QIDQ604289FDOQ604289

Authors Elad Priel, Arie Bussiba, Ilan Gilad, Zohar Yosibash 

Publication date 10 November 2010

Published in International Journal of Fracture (Search for Journal in Brave)

Full work available at URL https://doi.org/10.1007/s10704-007-9098-x

zbMATH Keywords

V-notchceramicsfailure initiationmixed-modegeneralized stress intensity factorsp-version FEA

Mathematics Subject Classification ID

Free convection (76R10) Stress concentrations, singularities in solid mechanics (74G70)

Recommendations

• Failure criteria for brittle elastic materials
• A failure criterion for brittle elastic materials under mixed-mode loading
• A 3-D failure initiation criterion from a sharp V-notch edge in elastic brittle structures
• Failure initiation at a blunt V-notch tip under mixed mode loading
• Fracture assessment of U-notches under mixed mode loading: two procedures based on the `equivalent local mode I' concept

Cites work

• A failure criterion for brittle elastic materials under mixed-mode loading
• Failure criteria for brittle elastic materials
• Fracture initiation at sharp notches: Correlation using critical stress intensities
• Strength or toughness? A criterion for crack onset at a notch

Cited in

(16)

• Fracture assessment of U-notches under mixed mode loading: two procedures based on the `equivalent local mode I' concept
• Stress-based criteria for brittle fracture in key-hole notches under mixed mode loading
• Computation of V-notch shape factors in four-point bend specimen for fracture tests on brittle materials
• Generalised stress intensity factors for rounded notches in plates under in-plane shear loading
• On the determination of crack initiation directions under mixed mode loading
• Failure initiation at a blunt V-notch tip under mixed mode loading
• \(T\)-stress effects on crack deflection: straight vs. curved crack advance
• Combined tension-shear fracture analysis of V-notches with end holes
• Two-dimensional fracture mechanics problems for solids with sharp and rounded V-notches
• Mixed mode I/II failure prediction of thin U-notched ductile steel plates with significant strain-hardening and large strain-to-failure: the fictitious material concept
• A 3-D failure initiation criterion from a sharp V-notch edge in elastic brittle structures
• On the most dangerous V-notch
• Determination of mode II fracture toughness for U-shaped notches using Brazilian disc specimen
• A failure criterion for brittle elastic materials under mixed-mode loading
• Failure criteria for linear elastic materials with U-notches
• Brittle failures at rounded V-notches: a finite fracture mechanics approach

This page was built for publication: Mixed mode failure criteria for brittle elastic V-notched structures

Report a bug (only for logged in users!)Click here to report a bug for this page (MaRDI item Q604289)